PP-GF30-03-AD3002-XH is a 30% long glass fiber reinforced, chemically coupled, and thermally stable polypropylene plastic particle.
General | ||
Form Resin Pellets | ||
Filler 30 % Long Glass Fiber | ||
Feature Good Thermal | Chemically Coupled | |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.12 g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 7000 MPa | ISO 527-2/1A |
Tensile Stress, Break | 110 MPa | ISO 527-2/1A/5 |
Tensile Strain, Break | 2.2 % | ISO 527-2/1A/5 |
Flexural Modulus | ISO 178 | |
23 °C | 7000 MPa | |
80 °C | 6500 MPa | |
Flexural Stress | ISO 178 | |
23 °C | 175 MPa | |
80 °C | 100 MPa | |
C harpy Notched Impact Strength | ISO 179 1eA | |
-30 °C | 22 kJ/m² | |
23 °C | 24 kJ/m² | |
C harpy Unnotched Impact Strength | ISO 179 1eU | |
-30 °C | 48 kJ/m² | |
23 °C | 55 kJ/m² | |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) | 158 °C | ISO 75-2/A |
Flame Rating(1 mm) | HB | UL 94 |
Processing | Nominal Value |
Drying Temperature<Injection> | 90 - 100 °C |
Drying Time<Injection> | 2.0 hr |
Suggested Max Moisture<Injection> | 0.20 % |
Rear Temperature<Injection> | 200 - 230 °C |
Middle Temperature<injection> | 220 - 240 °C |
Front Temperature<Injection> | 240 - 250 °C |
Nozzle Temperature<Injection> | 230 - 250 °C |
Processing Temp, Melt<Injection> | 230 - 270 °C |
Mold Temperature<Injection> | 30 - 70 °C |
Injection Rate<Injection> | Slow |
Back Pressure<Injection> | < 3.00 MPa |
Feeding Zone Temperature<Injection> | 20 - 50 °C |
Zone4 temperature<Injection> | 250 - 260 °C |
Hot Runner Temperature<Injection> | 230 - 270 °C |
PP-GF30-03-AD3002-XH is a 30% long glass fiber reinforced, chemically coupled, and thermally stable polypropylene plastic particle.
General | ||
Form Resin Pellets | ||
Filler 30 % Long Glass Fiber | ||
Feature Good Thermal | Chemically Coupled | |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.12 g/cm³ | ISO 1183 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 7000 MPa | ISO 527-2/1A |
Tensile Stress, Break | 110 MPa | ISO 527-2/1A/5 |
Tensile Strain, Break | 2.2 % | ISO 527-2/1A/5 |
Flexural Modulus | ISO 178 | |
23 °C | 7000 MPa | |
80 °C | 6500 MPa | |
Flexural Stress | ISO 178 | |
23 °C | 175 MPa | |
80 °C | 100 MPa | |
C harpy Notched Impact Strength | ISO 179 1eA | |
-30 °C | 22 kJ/m² | |
23 °C | 24 kJ/m² | |
C harpy Unnotched Impact Strength | ISO 179 1eU | |
-30 °C | 48 kJ/m² | |
23 °C | 55 kJ/m² | |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(1.8 MPa) | 158 °C | ISO 75-2/A |
Flame Rating(1 mm) | HB | UL 94 |
Processing | Nominal Value |
Drying Temperature<Injection> | 90 - 100 °C |
Drying Time<Injection> | 2.0 hr |
Suggested Max Moisture<Injection> | 0.20 % |
Rear Temperature<Injection> | 200 - 230 °C |
Middle Temperature<injection> | 220 - 240 °C |
Front Temperature<Injection> | 240 - 250 °C |
Nozzle Temperature<Injection> | 230 - 250 °C |
Processing Temp, Melt<Injection> | 230 - 270 °C |
Mold Temperature<Injection> | 30 - 70 °C |
Injection Rate<Injection> | Slow |
Back Pressure<Injection> | < 3.00 MPa |
Feeding Zone Temperature<Injection> | 20 - 50 °C |
Zone4 temperature<Injection> | 250 - 260 °C |
Hot Runner Temperature<Injection> | 230 - 270 °C |