Conductive Polypropylene Compound Recycled PP Granule PP Plastic Material

Form                                        Resin Pellets

Filler                                        Conductive agent

Feature                                    Electrically Conductive      Good Thermal                  Medium Flow

Usage                                       Industrial Parts                  Automotive                      Electrical

Physical                                                                                Nominal Value                                       Test Method

Density / Specific Gravity                                                    1.03 g/cm³                                             ASTM D792

Molding Shrinkage, Flow(3.2 mm)                                     1.2 - 1.4 %                                               ASTM D955

Mechanical                                                                            Nominal Value                                     Test Method

Tensile Strength                                                                   25.0 MPa                                               ASTM D638

Tensile Elongation, Break                                                   4.0 %                                                      ASTM D638

Flexural Modulus                                                                  1230 MPa                                               ASTM D790

Flexural Strength                                                                 41.0 MPa                                               ASTM D790

Notched Izod Impact(23 °C)                                                130 J/m                                                  ASTM D256

Thermal                                                                                 Nominal Value                                      Test Method

Deflection Temperature Under Load, Unannealed(1.8 MPa;4 mm)

65.0 °C                                                   ASTM D648

Electrical                                                                               Nominal Value                                       Test Method

Surface Resistivity                                                               1.0E+3 - 1.0E+5 ohms                           ASTM D257

Processing                                                                                                                                          Nominal Value

Drying Temperature<Injection>                                                                                                       80 °C

Drying Time<Injection>                                                                                                                    2.0 - 4.0 hr

Rear Temperature<Injection>                                                                                                            185 - 190 °C

Middle Temperature<injection>                                                                                                       190 - 195 °C

Front Temperature<Injection>                                                                                                         195 - 210 °C

Nozzle Temperature<Injection>                                                                                                       210 - 220 °C

Processing Temp, Melt<Injection>                                                                                                    190 - 220 °C

Mold Temperature<Injection>                                                                                                          60 - 90 °C