Conductive Internally Lubricated Wear-resistant And Flame Retardant Polycarbonate (PC) Resin Particles

Form

 Resin Pellets

Filler

15 % Carbon Fiber

5 % PTFE

Feature

Electrically Conductive

Good Hardness

 Abrasion Resistant

Light-Weight Structural

Super Strong (Carbon Fiber Filled)

 Internally Lubricated

Usage                               Industria

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.31

ASTM D792

Mechanical

Nominal Value

Test Method

Izod Impact, Unnotched(23 °C)

283 J/m

ASTM D4812

Izod Impact, Notched(23 °C)

53 J/m

ASTM D256

Instrumented Dart Impact, Energy at Peak(23 °C)

11 J

ASTM D3763

Tensile Stress, Yield(5 mm/min;Type I)

111 MPa

ASTM D638

Tensile Stress, Break(5 mm/min;Type I)

111 MPa

ASTM D638

Tensile Strain, Break(5 mm/min;Type I)

4.1 %

ASTM D638

Flexural Stress, break

1.3 mm/min;50 mm;span

2.6 mm/min;100 mm;Span

160 MPa

154 MPa

ASTM D790

Flexural Modulus

1.3 mm/min;50 mm;span

2.6 mm/min;100 mm;Span

9080 MPa

8410 MPa

ASTM D790

Coefficient of Friction, Steel, Static

0.41

ASTM D1894

Coefficient Of Friction, Steel, Kinetic

0.19

ASTM D1894

UL Recognized(≥ 1.5 mm)

V-0

UL 94

Heat Deflection Temperature[HDT], Unannealed

0.45 MPa;3.2 mm

3.2 mm;1.82 MPa 0.45 MPa;6.4 mm

1.82 MPa;6.4 mm

141 °C

137 °C

144 °C

139 °C

ASTM D648

Relative Temp Index, Elec

80 °C

UL 746B

Relative Temp Index, Mechanical with Impact

80 °C

UL 746B

Relative Temp Index, Mechanical without Impact

80 °C

UL 746B

Electrical

Nominal Value

Test Method

Surface Resistivity

1.0E+04 ohms

ASTM D257

Static Decay(5000V to <50V)

< 0.01 Seconds

FTMS101B

Processing

Nominal Value

Drying Temperature<Injection>

120 °C

Drying Time<Injection>

3 - 4 hrs

Drying Time, Cumulative<Injection>

48 hrs

Maximum Moisture Content<Injection>

0.02 %

Melt Temperature<Injection>

290 - 315 °C

Nozzle Temperature<Injection>

290 - 315 °C

Front, Zone 3 Temperature<Injection>

290 - 315 °C

Middle, Zone 2 Temperature<Injection>

280 - 305 °C

Rear, Zone 1 Temperature<Injection>

275 - 295 °C

Mold Temperature<Injection>

70 - 105 °C

Back Pressure<Injection>

0.3 - 0.7 MPa

Screw Speed <Injection>

40 - 70 rpm

Shot To Cylinder Size<Injection>

40 - 60 %

Vent Depth <Injection>

0.025 - 0.076 mm