LUX740C-XH
FOREVER
1 What is the technical data sheet for the transparent UV stabilized F1 Rating polycarbonate PC resins?
Product Description | |||||
LUX7430C-XH is an easy-to-mold, injection-moldable thermoplastic polymer widely used in automotive and electrical industries. LUX7430C-XH has excellent heat resistance, flame retardancy with an UL-94 V0 rating at 1.2mm, and UV stabilization properties allowing outdoor applications. This non-filled polymer is available in clear, transparent, and opaque color options and can be molded into various shapes and sizes. With its combination of excellent properties, LUX7430C-XH is an ideal choice for various applications in the automotive and electrical industry. | |||||
General | |||||
Form | Pellets Resins | ||||
Feature | F1 | Non-Brominated & Non-Chlorinated Flame Retardant | |||
|
|
| |||
Physical | Value | Test Method | |||
Density / Specific Gravity |
1.20 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 10 g/10min | ASTM D1238 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 9 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion |
| UL 746C | |||
Mechanical | Value | Test Method | |||
Izod Impact, Unnotched 23 °C -30 °C |
NB J/m NB J/m | ASTM D4812 | |||
Izod Impact, Notched 23 °C -30 °C |
100 J/m 81 J/m | ASTM D256 | |||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² | ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
9 kJ/m² 8 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
10 kJ/m² 7 kJ/m² | ISO 179 1eA |
Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
55 MPa 53 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
55 % 56 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2520 MPa 2350 MPa |
ASTM D638 ISO 527 |
Flexural Stress, 1.3 mm/min;50 mm;span 2 mm/min |
107 MPa 101 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2450 MPa 2450 MPa |
ASTM D790 ISO 178 |
1 What is the technical data sheet for the transparent UV stabilized F1 Rating polycarbonate PC resins?
Product Description | |||||
LUX7430C-XH is an easy-to-mold, injection-moldable thermoplastic polymer widely used in automotive and electrical industries. LUX7430C-XH has excellent heat resistance, flame retardancy with an UL-94 V0 rating at 1.2mm, and UV stabilization properties allowing outdoor applications. This non-filled polymer is available in clear, transparent, and opaque color options and can be molded into various shapes and sizes. With its combination of excellent properties, LUX7430C-XH is an ideal choice for various applications in the automotive and electrical industry. | |||||
General | |||||
Form | Pellets Resins | ||||
Feature | F1 | Non-Brominated & Non-Chlorinated Flame Retardant | |||
|
|
| |||
Physical | Value | Test Method | |||
Density / Specific Gravity |
1.20 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 10 g/10min | ASTM D1238 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 9 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion |
| UL 746C | |||
Mechanical | Value | Test Method | |||
Izod Impact, Unnotched 23 °C -30 °C |
NB J/m NB J/m | ASTM D4812 | |||
Izod Impact, Notched 23 °C -30 °C |
100 J/m 81 J/m | ASTM D256 | |||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² | ISO 180/1U |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
9 kJ/m² 8 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
10 kJ/m² 7 kJ/m² | ISO 179 1eA |
Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
55 MPa 53 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
55 % 56 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2520 MPa 2350 MPa |
ASTM D638 ISO 527 |
Flexural Stress, 1.3 mm/min;50 mm;span 2 mm/min |
107 MPa 101 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2450 MPa 2450 MPa |
ASTM D790 ISO 178 |