Chemical Resistance And High Toughness Resin Plastic Material PC Raw Material

Form

Resin Pellets

Filler

20% glass fiber

Feature

Good Hardness

Lds

Non-Brominated & Non- Chlorinated Flame Retardant

Structural

Non-Chlorinated

Circuit Solution

Usage

Consumer                          Laser Direct Structuring

Building and Construction

Electrical

Physical

Nominal Value

Test Method

Melt Flow Rate[MFR]

300 °C;2.16 kgf

300 °C;1.2 kgf

17 g/10min

10 g/10min

ASTM D1238

Density / Specific Gravity

1.4 g/cm³

ASTM D792

Izod Impact, Notched

23 °C

80 J/m

ASTM D256

80*10*4;23 °C

8 kJ/m²

ISO 180/1A

Izod Impact, Unnotched

23 °C

450 J/m

ASTM D4812

80*10*4;23 °C

26 kJ/m²

ISO 180/1U

C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0)

8 kJ/m²

ISO 179 1eA

C harpy Impact, Unnotched(23 °C;Edgew;80*10*4;sp =62 mm 0)

30 kJ/m²

ISO 179 1eU

Tensile Stress, Break

5 mm/min;Type I

85 MPa

ASTM D638

5 mm/min

86 MPa

ISO 527

Tensile Strain, Break

5 mm/min;Type I

2.5 %

ASTM D638

5 mm/min

2.5 %

ISO 527

Tensile Modulus

5 mm/min

7000 MPa

ASTM D638

1 mm/min

6900 MPa

ISO 527

Flexural Modulus

1.3 mm/min;50 mm;span

6000 MPa

ASTM D790

2 mm/min

6400 MPa

ISO 178

Flexural Strength

1.3 mm/min;50 mm;span

125 MPa

ASTM D790

2 mm/min

130 MPa

ISO 178

Thermal

Nominal Value

Test Method

Heat Deflection Temperature[HDT], Unannealed

0.45 MPa;3.2 mm

3.2 mm;1.82 MPa

124 °C

118 °C

ASTM D648

Processing

Nominal Value

Drying Temperature<Injection>

110 - 120 °C

Drying Time<Injection>

3 - 4 hrs

Melt Temperature<Injection>

290 - 310 °C

Nozzle Temperature<Injection>

285 - 310 °C

Front, Zone 3 Temperature<Injection>

285 - 310 °C

Middle, Zone 2 Temperature<Injection>

285 - 310 °C

Rear, Zone 1 Temperature<Injection>

285 - 310 °C

Mold Temperature<Injection>

100 - 130 °C

Back Pressure<Injection>

0.1 - 0.3 MPa

Screw Speed <Injection>

50 - 150 rpm