HCX1640-XH
Forever
HCX1640-XH is a specifically formulated Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend that is designed to meet the biocompatibility requirements for use in medical devices and pharmaceutical applications. It offers enhanced heat resistance, improved flow properties, and superior impact resistance compared to standard PC/ABS blends. Furthermore, this grade complies with our rigorous healthcare management of change policy to ensure the highest quality and safety standards.
General | ||
Form | ||
Impact Biocompatible Excellent Processability | ||
Usage |
|
|
Physical | Nominal Value | Test Method |
Density / Specific Gravity |
1.15 1.15 g/cm³ |
ASTM D792 ISO 1183 |
Melt Flow Rate[MFR](260 °C;5 kgf) | 19 g/10min | ASTM D1238 |
Water Absorption(23 °C;saturated) | 0.4 % | ISO 62-1 |
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 |
Melt Volume Rate, MVR(5 kg;MVR at 260 °C) | 18 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 550 J/m | ASTM D256 |
-30 °C | 300 J/m | ASTM D256 |
80*10*4;23 °C | 40 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 20 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 |
Izod Impact, Unnotched | ISO 180/1U | |
80*10*4;23 °C | NB kJ/m² | |
80*10*4;-30 °C | NB kJ/m² | |
C harpy Impact, V-Notched | ISO 179 1eA | |
23 °C;Edgew;80*10*4;sp =62 mm 0 | 40 kJ/m² | |
-30 °C;Edgew;80*10*4;sp =62 mm 0 | 20 kJ/m² | |
C harpy Impact, Unnotched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield | ||
50 mm/min;Type I | 55 MPa | ASTM D638 |
50 mm/min | 55 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 50 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 5 % | ASTM D638 |
50 mm/min | 5 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | > 50 % | ASTM D638 |
50 mm/min | > 50 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 2400 MPa | ASTM D638 |
1 mm/min | 2400 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 85 MPa | ASTM D790 |
2 mm/min | 85 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2300 MPa | ASTM D790 |
2 mm/min | 2300 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Vicat Softening Temperature | ||
Rate B/50 | 130 °C | ASTM D1525 |
Rate B/50 | 130 °C | ISO 306 |
Rate B/120 | 132 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
122 °C 108 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.0E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.0E-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 7.0E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.0E-05 1/°C | ISO 11359-2 |
HDT/Af(1.8) | 108 °C | ISO 75/Af |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 - 110 °C | |
Drying Time<Injection> | 2 - 4 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 260 - 290 °C | |
Nozzle Temperature<Injection> | 240 - 280 °C | |
Front, Zone 3 Temperature<Injection> | 250 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 250 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 260 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 90 °C |
HCX1640-XH is a specifically formulated Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend that is designed to meet the biocompatibility requirements for use in medical devices and pharmaceutical applications. It offers enhanced heat resistance, improved flow properties, and superior impact resistance compared to standard PC/ABS blends. Furthermore, this grade complies with our rigorous healthcare management of change policy to ensure the highest quality and safety standards.
General | ||
Form | ||
Impact Biocompatible Excellent Processability | ||
Usage |
|
|
Physical | Nominal Value | Test Method |
Density / Specific Gravity |
1.15 1.15 g/cm³ |
ASTM D792 ISO 1183 |
Melt Flow Rate[MFR](260 °C;5 kgf) | 19 g/10min | ASTM D1238 |
Water Absorption(23 °C;saturated) | 0.4 % | ISO 62-1 |
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 |
Melt Volume Rate, MVR(5 kg;MVR at 260 °C) | 18 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 550 J/m | ASTM D256 |
-30 °C | 300 J/m | ASTM D256 |
80*10*4;23 °C | 40 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 20 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 |
Izod Impact, Unnotched | ISO 180/1U | |
80*10*4;23 °C | NB kJ/m² | |
80*10*4;-30 °C | NB kJ/m² | |
C harpy Impact, V-Notched | ISO 179 1eA | |
23 °C;Edgew;80*10*4;sp =62 mm 0 | 40 kJ/m² | |
-30 °C;Edgew;80*10*4;sp =62 mm 0 | 20 kJ/m² | |
C harpy Impact, Unnotched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield | ||
50 mm/min;Type I | 55 MPa | ASTM D638 |
50 mm/min | 55 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 50 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 5 % | ASTM D638 |
50 mm/min | 5 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | > 50 % | ASTM D638 |
50 mm/min | > 50 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 2400 MPa | ASTM D638 |
1 mm/min | 2400 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 85 MPa | ASTM D790 |
2 mm/min | 85 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2300 MPa | ASTM D790 |
2 mm/min | 2300 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Vicat Softening Temperature | ||
Rate B/50 | 130 °C | ASTM D1525 |
Rate B/50 | 130 °C | ISO 306 |
Rate B/120 | 132 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
122 °C 108 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.0E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.0E-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 7.0E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.0E-05 1/°C | ISO 11359-2 |
HDT/Af(1.8) | 108 °C | ISO 75/Af |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 - 110 °C | |
Drying Time<Injection> | 2 - 4 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 260 - 290 °C | |
Nozzle Temperature<Injection> | 240 - 280 °C | |
Front, Zone 3 Temperature<Injection> | 250 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 250 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 260 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 90 °C |
Resin Pellets