MD206U-XH
Forever
MD206U-XH is a specialized 20% mineral-filled polypropylene compound designed for injection molding applications. It is specifically formulated for automotive interior parts that demand a perfect balance between impact strength, stiffness, and superior surface quality. Additionally, it offers excellent UV and weathering resistance. MD206U-XH is well-suited for various automotive components such as door panels, pockets, consoles, handles, bumper reinforcement parts, and cowl vent grilles.
General |
Form |
Filler |
Feature |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.04 g/cm³ ISO 1183 |
Melt Flow ISO 1133 |
2.16 kg;230 °C 7.0 g/10min |
5 kg;230 °C 24 g/10min |
Ball Indentation Hardness 59.0 MPa ISO 2039 |
Mechanical Nominal Value Test Method |
Tensile Strength, Yield(50 mm/min) 24.99 MPa ISO 527-2 |
Elongation at Yield(50 mm/min) 5.0 % ISO 527-2 |
Flexural Modulus(5 mm/min) 2250 MPa ISO 178 |
C harpy Impact Unnotched ISO 179 1eU |
Temperature; 23 °C No Break |
Temperature; -40 °C 33 kJ/m² |
Temperature; -20 °C 37 kJ/m² |
C harpy Impact, Notched ISO 179 1eA |
Temperature; 23 °C 12 kJ/m² |
Temperature; -20 °C 2.5 kJ/m² |
Thermal | Nominal Value | Test Method |
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
112 °C 60.4 °C | ISO 75-2 |
Vicat Softening Point 50 N;Rate B 10 N;Rate A |
80.0 °C 150 °C | ISO 306 |
Processing | Nominal Value | |
Melt Temperature | 210 - 260 °C | |
Mold Temperature | 30.0 - 50.0 °C |
MD206U-XH is a specialized 20% mineral-filled polypropylene compound designed for injection molding applications. It is specifically formulated for automotive interior parts that demand a perfect balance between impact strength, stiffness, and superior surface quality. Additionally, it offers excellent UV and weathering resistance. MD206U-XH is well-suited for various automotive components such as door panels, pockets, consoles, handles, bumper reinforcement parts, and cowl vent grilles.
General |
Form |
Filler |
Feature |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.04 g/cm³ ISO 1183 |
Melt Flow ISO 1133 |
2.16 kg;230 °C 7.0 g/10min |
5 kg;230 °C 24 g/10min |
Ball Indentation Hardness 59.0 MPa ISO 2039 |
Mechanical Nominal Value Test Method |
Tensile Strength, Yield(50 mm/min) 24.99 MPa ISO 527-2 |
Elongation at Yield(50 mm/min) 5.0 % ISO 527-2 |
Flexural Modulus(5 mm/min) 2250 MPa ISO 178 |
C harpy Impact Unnotched ISO 179 1eU |
Temperature; 23 °C No Break |
Temperature; -40 °C 33 kJ/m² |
Temperature; -20 °C 37 kJ/m² |
C harpy Impact, Notched ISO 179 1eA |
Temperature; 23 °C 12 kJ/m² |
Temperature; -20 °C 2.5 kJ/m² |
Thermal | Nominal Value | Test Method |
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
112 °C 60.4 °C | ISO 75-2 |
Vicat Softening Point 50 N;Rate B 10 N;Rate A |
80.0 °C 150 °C | ISO 306 |
Processing | Nominal Value | |
Melt Temperature | 210 - 260 °C | |
Mold Temperature | 30.0 - 50.0 °C |
Resin Pellets