Abrasion Resistant Wholesale POM Plastic Raw Material Polyoxymethylene Resin

Dongguan Forever Co.,Ltd is the manufacture of the china origin cheap UV stablized PC polycarbonate Granules Polymer Resin
  • FX-11-XH

  • Forever

FX-11-XH has good comprehensive performance and coloring properties, with high elastic modulus, high stiffness and hardness, and a specific strength and stiffness close to that of metals; Excellent tensile strength, bending strength, creep and fatigue resistance, repeated impact resistance, and excellent load recovery.


Form                                        Resin Pellets

Feature                                    Abrasion Resistant

Usage                                       Automotive Electronics    Automotive

Physical                                                                                Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.39 g/cm³                                             ISO 1183

Melt Mass-Flow Rate, MFR(190 °C;2.16 kg)                        10 g/10min                                             ISO 1133

Melt Volume-Flow Rate, MVR(190 °C;2.16 kg)                   8.60 cm³/10 min                                    ISO 1133

Molding Shrinkage, Flow(3 mm)                                         2.1 %                                                      Internal Method

Water Absorption - 60% RH(23 °C)                                     0.22 %                                                    Internal Method

Mechanical                                                                            Nominal Value                                     Test Method

Tensile Modulus                                                                  2700 MPa                                               ISO 527-2/1

Tensile Stress, Yield                                                             55.0 MPa                                                ISO 527-2/50

Tensile Strain, Yield                                                             9.0 %                                                      ISO 527-2/50

Tensile Strain, Break                                                             35 %                                                       ISO 527-2/50

Flexural Modulus(2 mm/min)                                              2500 MPa                                              ISO 178

Flexural Stress(2 mm/min)                                                   81.0 MPa                                                ISO 178

C harpy Notched Impact Strength(23 °C)                            7.0 kJ/m²                                                ISO 179

C harpy Unnotched Impact Strength(23 °C)                        200 kJ/m²                                               ISO 179

Thermal                                                                                 Nominal Value                                      Test Method

Heat Deflection Temperature, Unannealed

0.45 MPa                                                                            156 °C                                                     ISO 75-2/B

1.8 MPa                                                                               95.0 °C                                                    ISO 75-2/A

CLTE, Flow                                                                           1.1E-4 cm/cm/°C                                    ISO 11359-2

CLTE, Transverse                                                                  1.1E-4 cm/cm/°C                                  ISO 11359-2

Flame Rating(0.8 mm)                                                         HB                                                            UL 94


Nominal Value

Test Method

Surface Resistivity

1.0E+16 ohms

IEC 60093

Volume Resistivity

1.0E+14 ohms ·cm

IEC 60093

Electric Strength

1 mm

36 kV/mm

ASTM D150;IEC 60250

3 mm

19 kV/mm

IEC 60243-1

Comparative Tracking Index

600 V

IEC 60112


Nominal Value

Drying Temperature - Hot Air Dryer<Injection>

80 °C

Drying Time - Hot Air Dryer<Injection>

3.0 - 4.0 hr

Rear Temperature<Injection>

170 °C

Middle Temperature<injection>

180 °C

Front Temperature<Injection>

190 °C

Nozzle Temperature<Injection>

180 - 210 °C

Mold Temperature<Injection>

60 - 80 °C

Injection Pressure<Injection>

50.0 - 100 MPa

Injection Rate<Injection>


Screw Speed <Injection>

80 - 120 rpm

Melting Point

166 °C

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D