P2HGV-XH
Forever
P2HGV-XH is a type of injection molding grade material that contains 16.5% glass fiber reinforcement. This material is known for its excellent rigidity and resistance to heat. It is characterized by its high stiffness, strength, and heat resistance. P2HGV-XH is commonly used in the manufacturing of semi-structural automotive parts and gambling machines.
General | ||||
Form | Resin Pellets | |||
Filler | 16 % Glass Fiber | |||
Feature | Good Thermal | High Mechanical Strength Good Hardness
| ||
Usage |
| |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.16 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 3.0 cm³/10 min | ISO 1133 | ||
Molding Shrinkage | 0.20 - 0.40 % | ISO 294-4 | ||
Ash Content | 16 % | |||
Ball Indentation Hardness | 135 MPa | ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 5500 MPa | ISO 527-2 | ||
Tensile Stress, Yield(23 °C) | 74.0 MPa | ISO 527-2 | ||
Tensile Stress, Break(23 °C) | 74.0 MPa | ISO 527-2 | ||
Tensile Strain, Break(23 °C) | 2.0 % | ISO 527-2 | ||
Flexural Modulus(23 °C) | 5400 MPa | ISO 178 | ||
Flexural Stress(23 °C) | 101 MPa | ISO 178 | ||
C harpy Notched Impact Strength -30 °C 23 °C |
5.0 kJ/m² 6.0 kJ/m² | ISO 179 1eA | ||
C harpy Unnotched Impact Strength -30 °C 23 °C |
20 kJ/m² 18 kJ/m² | ISO 179 1eU | ||
Notched Izod Impact Strength -30 °C 23 °C |
5.0 kJ/m² 7.0 kJ/m² | ISO 180/1A | ||
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Annealed 0.45 MPa;4 h;80 °C 1.8 MPa;4 h;80 °C |
106 °C 102 °C |
ISO 75-2/B ISO 75-2/A |
Vicat Softening Temperature |
107 °C 105 °C |
ISO 306/B120 ISO 306/B50 |
CLTE, Flow | 4.0E-5 cm/cm/°C | ISO 11359-1 |
Burning rate(2 mm) | 20 mm/min | ISO 3795 |
Flame Rating(1.5 mm) | HB | IEC 60695-11-10 |
Glow Wire Flammability Index(2 mm) | 700 °C | IEC 60695-2-12 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+14 ohms | IEC 62631-3-1 |
Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 62631-3-1 |
Electric Strength(1 mm) | 32 kV/mm | IEC 60243-1 |
Relative Permittivity 100 Hz 1.0e+6 Hz |
2.90 3.10 | IEC 62631-2-1 |
Dissipation Factor 100 Hz 1.0e+6 Hz |
9.0E-3 6.0E-3 | IEC 62631-2-1 |
Comparative Tracking Index | 575 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Processing Temp, Melt<Injection> | 230 - 260 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Injection Velocity<Injection> | 14 m/min |
P2HGV-XH is a type of injection molding grade material that contains 16.5% glass fiber reinforcement. This material is known for its excellent rigidity and resistance to heat. It is characterized by its high stiffness, strength, and heat resistance. P2HGV-XH is commonly used in the manufacturing of semi-structural automotive parts and gambling machines.
General | ||||
Form | Resin Pellets | |||
Filler | 16 % Glass Fiber | |||
Feature | Good Thermal | High Mechanical Strength Good Hardness
| ||
Usage |
| |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.16 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 3.0 cm³/10 min | ISO 1133 | ||
Molding Shrinkage | 0.20 - 0.40 % | ISO 294-4 | ||
Ash Content | 16 % | |||
Ball Indentation Hardness | 135 MPa | ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus | 5500 MPa | ISO 527-2 | ||
Tensile Stress, Yield(23 °C) | 74.0 MPa | ISO 527-2 | ||
Tensile Stress, Break(23 °C) | 74.0 MPa | ISO 527-2 | ||
Tensile Strain, Break(23 °C) | 2.0 % | ISO 527-2 | ||
Flexural Modulus(23 °C) | 5400 MPa | ISO 178 | ||
Flexural Stress(23 °C) | 101 MPa | ISO 178 | ||
C harpy Notched Impact Strength -30 °C 23 °C |
5.0 kJ/m² 6.0 kJ/m² | ISO 179 1eA | ||
C harpy Unnotched Impact Strength -30 °C 23 °C |
20 kJ/m² 18 kJ/m² | ISO 179 1eU | ||
Notched Izod Impact Strength -30 °C 23 °C |
5.0 kJ/m² 7.0 kJ/m² | ISO 180/1A | ||
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Annealed 0.45 MPa;4 h;80 °C 1.8 MPa;4 h;80 °C |
106 °C 102 °C |
ISO 75-2/B ISO 75-2/A |
Vicat Softening Temperature |
107 °C 105 °C |
ISO 306/B120 ISO 306/B50 |
CLTE, Flow | 4.0E-5 cm/cm/°C | ISO 11359-1 |
Burning rate(2 mm) | 20 mm/min | ISO 3795 |
Flame Rating(1.5 mm) | HB | IEC 60695-11-10 |
Glow Wire Flammability Index(2 mm) | 700 °C | IEC 60695-2-12 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 1.0E+14 ohms | IEC 62631-3-1 |
Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 62631-3-1 |
Electric Strength(1 mm) | 32 kV/mm | IEC 60243-1 |
Relative Permittivity 100 Hz 1.0e+6 Hz |
2.90 3.10 | IEC 62631-2-1 |
Dissipation Factor 100 Hz 1.0e+6 Hz |
9.0E-3 6.0E-3 | IEC 62631-2-1 |
Comparative Tracking Index | 575 V | IEC 60112 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 2.0 - 4.0 hr | |
Processing Temp, Melt<Injection> | 230 - 260 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Injection Velocity<Injection> | 14 m/min |
And Rigidity