732E-XH
Forever
The 732E-XH product is a 30% glass/mineral reinforced PBT granular plastic material. Has excellent thermal performance, low shrinkage and warpage. Easy to flow.
General | |||||
Form |
| ||||
Filler |
| ||||
Feature |
Low Shrinkage |
| |||
Automotive Under The Hood | Automotive | ||||
Usage | Automotive Lighting | Electrical | |||
| |||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.51 g/cm³ | ASTM D792 | |||
Specific Volume | 0.660 cm³/g | ASTM D792 | |||
Molding Shrinkage, Across Flow | Internal Method | ||||
1.5 - 3.2 mm | 0.40 - 0.60 % | ||||
3.2 - 4.6 mm | 0.60 - 0.80 % | ||||
Molding Shrinkage, Flow | Internal Method | ||||
1.5 - 3.2 mm | 0.30 - 0.40 % | ||||
3.2 - 4.6 mm | 0.40 - 0.60 % | ||||
Water Absorption(24 hr) | 0.070 % | ASTM D570 | |||
Rockwell Hardness, R-Scale | 109 | ASTM D785 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength, Break(5 mm/min;Type I) | 82.0 MPa | ASTM D638 | |||
Tensile Elongation, Break(5 mm/min;Type I) | 2.0 % | ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 6890 MPa | ASTM D790 | |||
Flexural Strength, Break(1.3 mm/min;50 mm;Span) | 124 MPa | ASTM D790 | |||
Notched Izod Impact(23 °C) | 100 J/m | ASTM D256 | |||
Unnotched Izod Impact(23 °C) | 530 J/m | ASTM D4812 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
215 °C 198 °C | ASTM D648 |
CLTE, Flow -40 - 40 °C 60 - 138 °C |
2.5E-5 cm/cm/°C 2.5E-5 cm/cm/°C | ASTM E831 |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.0e+17 ohms ·cm | ASTM D257 |
Dielectric Strength, in Oil(3.2 mm) | 18 kV/mm | ASTM D149 |
Dielectric Constant 60 Hz 5.0e+4 Hz 1.0e+6 Hz |
3.53 3.53 3.32 | ASTM D150 |
Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
8.0E-3 8.0E-3 0.013 | ASTM D150 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 80 % | |
Rear Temperature<Injection> | 245 - 255 °C | |
Middle Temperature<injection> | 250 - 260 °C | |
Front Temperature<Injection> | 255 - 265 °C | |
Nozzle Temperature<Injection> | 255 - 270 °C | |
Processing Temp, Melt<Injection> | 255 - 275 °C | |
Mold Temperature<Injection> | 65 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 50 - 80 rpm | |
Vent Depth <Injection> | 0.025 - 0.038 mm | |
Injection, Drying Time, Cumulative<Injection> | 12 hrs |
The 732E-XH product is a 30% glass/mineral reinforced PBT granular plastic material. Has excellent thermal performance, low shrinkage and warpage. Easy to flow.
General | |||||
Form |
| ||||
Filler |
| ||||
Feature |
Low Shrinkage |
| |||
Automotive Under The Hood | Automotive | ||||
Usage | Automotive Lighting | Electrical | |||
| |||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.51 g/cm³ | ASTM D792 | |||
Specific Volume | 0.660 cm³/g | ASTM D792 | |||
Molding Shrinkage, Across Flow | Internal Method | ||||
1.5 - 3.2 mm | 0.40 - 0.60 % | ||||
3.2 - 4.6 mm | 0.60 - 0.80 % | ||||
Molding Shrinkage, Flow | Internal Method | ||||
1.5 - 3.2 mm | 0.30 - 0.40 % | ||||
3.2 - 4.6 mm | 0.40 - 0.60 % | ||||
Water Absorption(24 hr) | 0.070 % | ASTM D570 | |||
Rockwell Hardness, R-Scale | 109 | ASTM D785 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength, Break(5 mm/min;Type I) | 82.0 MPa | ASTM D638 | |||
Tensile Elongation, Break(5 mm/min;Type I) | 2.0 % | ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 6890 MPa | ASTM D790 | |||
Flexural Strength, Break(1.3 mm/min;50 mm;Span) | 124 MPa | ASTM D790 | |||
Notched Izod Impact(23 °C) | 100 J/m | ASTM D256 | |||
Unnotched Izod Impact(23 °C) | 530 J/m | ASTM D4812 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
215 °C 198 °C | ASTM D648 |
CLTE, Flow -40 - 40 °C 60 - 138 °C |
2.5E-5 cm/cm/°C 2.5E-5 cm/cm/°C | ASTM E831 |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.0e+17 ohms ·cm | ASTM D257 |
Dielectric Strength, in Oil(3.2 mm) | 18 kV/mm | ASTM D149 |
Dielectric Constant 60 Hz 5.0e+4 Hz 1.0e+6 Hz |
3.53 3.53 3.32 | ASTM D150 |
Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
8.0E-3 8.0E-3 0.013 | ASTM D150 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 80 % | |
Rear Temperature<Injection> | 245 - 255 °C | |
Middle Temperature<injection> | 250 - 260 °C | |
Front Temperature<Injection> | 255 - 265 °C | |
Nozzle Temperature<Injection> | 255 - 270 °C | |
Processing Temp, Melt<Injection> | 255 - 275 °C | |
Mold Temperature<Injection> | 65 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 50 - 80 rpm | |
Vent Depth <Injection> | 0.025 - 0.038 mm | |
Injection, Drying Time, Cumulative<Injection> | 12 hrs |