NS0031-XH
FOREVER
NS0031-XH is the ultimate product for shielding you against electromagnetic and radio frequency interferences.
It is made from a blend of Polycarbonate and Acrylonitrile Butadiene Styrene (PC/ABS) mixed with 15% stainless steel fiber. This compound is not only excellent for EMI/RFI shielding but it is also conductive, ensuring seamless transmission of electric current.
The product is also non-brominated and non-chlorinated, which makes it non-toxic and environment-friendly. Additionally, NS0031-XH has flame retardant properties and has been rated V-0/5VA by UL.
General | ||||
Form | Resin Pellets | |||
Filler | 15 % Stainless Steel Fiber | |||
Feature | Electrically Conductive Chlorinated Flame
Non-Chlorinated | |||
|
|
| ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.33 1.33 g/cm³ | ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.59 % | SABIC Method | ||
Melt Flow Rate[MFR](280 °C;5 kgf) | 12.3 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.2 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 | ||
Melt Volume Rate, MVR(10 kg;MVR at 265 °C) | 31 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C | 686 J/m 588 J/m 39 kJ/m² 39 kJ/m² | ASTM D4812 ASTM D4812 ISO 180/1U ISO 180/1U | ||
Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C | 55 J/m 43 J/m 5 kJ/m² 5 kJ/m² | ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A | ||
Multiaxial Impact | 7 J | ISO 6603 |
Charpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp=62 mm 0) | 4 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield 5 mm/min;Type I 5 mm/min | 61 MPa 59 MPa | ASTM D638 ISO 527 |
Tensile Stress, Break 5 mm/min;Type I 5 mm/min | 57 MPa 55 MPa | ASTM D638 ISO 527 |
Tensile Strain, Yield 5 mm/min;Type I 5 mm/min | 3.4 % 3.2 % | ASTM D638 ISO 527 |
Tensile Strain, Break 5 mm/min;Type I 5 mm/min | 3.7 % 4.4 % | ASTM D638 ISO 527 |
Tensile Modulus 5 mm/min 1 mm/min | 3120 MPa 3000 MPa | ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min | 95 MPa 102 MPa | ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min | 2970 MPa 3090 MPa | ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 2 mm ≥ 1.5 mm | 5VB V-0 | UL 94 |
Vicat Softening Temperature | ||
Rate B/50 | 109 °C | ASTM D1525 |
Rate B/50 | 109 °C | ISO 306 |
Rate B/120 | 112 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 96 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -40 - 40 °C | 5.7E-05 1/°C 5.5e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -40 - 40 °C | 6.6E-05 1/°C 6.4e-05 1/°C | ASTM E831 ISO 11359-2 |
HDT/Af(1.8) | 98 °C | ISO 75/Af |
Relative Temp Index, Mechanical with Impact | 85 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 85 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.0E+07 ohms·cm | ASTM D257 |
Surface Resistivity | 1.0E+05 ohms | ASTM D257 |
Static Decay(5000V to <50V) | < 0.01 Seconds | FTMS101B |
Shielding Effectivness @ 3Mm | 47 dB | SABIC Method |
Processing | Nominal Value |
Drying Temperature<Injection> | 85 - 90 °C |
Drying Time<Injection> | 3 - 4 hrs |
Maximum Moisture Content<Injection> | 0.04 % |
Melt Temperature<Injection> | 270 - 300 °C |
Nozzle Temperature<Injection> | 265 - 300 °C |
Front, Zone 3 Temperature<Injection> | 265 - 300 °C |
Middle, Zone 2 Temperature<Injection> | 260 - 300 °C |
Rear, Zone 1 Temperature<Injection> | 260 - 300 °C |
Mold Temperature<Injection> | 60 - 90 °C |
Back Pressure<Injection> | 4 MPa |
Screw Speed<Injection> | 30 - 100 rpm |
NS0031-XH is the ultimate product for shielding you against electromagnetic and radio frequency interferences.
It is made from a blend of Polycarbonate and Acrylonitrile Butadiene Styrene (PC/ABS) mixed with 15% stainless steel fiber. This compound is not only excellent for EMI/RFI shielding but it is also conductive, ensuring seamless transmission of electric current.
The product is also non-brominated and non-chlorinated, which makes it non-toxic and environment-friendly. Additionally, NS0031-XH has flame retardant properties and has been rated V-0/5VA by UL.
General | ||||
Form | Resin Pellets | |||
Filler | 15 % Stainless Steel Fiber | |||
Feature | Electrically Conductive Chlorinated Flame
Non-Chlorinated | |||
|
|
| ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.33 1.33 g/cm³ | ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.59 % | SABIC Method | ||
Melt Flow Rate[MFR](280 °C;5 kgf) | 12.3 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.2 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 | ||
Melt Volume Rate, MVR(10 kg;MVR at 265 °C) | 31 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Unnotched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C | 686 J/m 588 J/m 39 kJ/m² 39 kJ/m² | ASTM D4812 ASTM D4812 ISO 180/1U ISO 180/1U | ||
Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C | 55 J/m 43 J/m 5 kJ/m² 5 kJ/m² | ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A | ||
Multiaxial Impact | 7 J | ISO 6603 |
Charpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp=62 mm 0) | 4 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield 5 mm/min;Type I 5 mm/min | 61 MPa 59 MPa | ASTM D638 ISO 527 |
Tensile Stress, Break 5 mm/min;Type I 5 mm/min | 57 MPa 55 MPa | ASTM D638 ISO 527 |
Tensile Strain, Yield 5 mm/min;Type I 5 mm/min | 3.4 % 3.2 % | ASTM D638 ISO 527 |
Tensile Strain, Break 5 mm/min;Type I 5 mm/min | 3.7 % 4.4 % | ASTM D638 ISO 527 |
Tensile Modulus 5 mm/min 1 mm/min | 3120 MPa 3000 MPa | ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min | 95 MPa 102 MPa | ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min | 2970 MPa 3090 MPa | ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 2 mm ≥ 1.5 mm | 5VB V-0 | UL 94 |
Vicat Softening Temperature | ||
Rate B/50 | 109 °C | ASTM D1525 |
Rate B/50 | 109 °C | ISO 306 |
Rate B/120 | 112 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 96 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -40 - 40 °C | 5.7E-05 1/°C 5.5e-05 1/°C | ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -40 - 40 °C | 6.6E-05 1/°C 6.4e-05 1/°C | ASTM E831 ISO 11359-2 |
HDT/Af(1.8) | 98 °C | ISO 75/Af |
Relative Temp Index, Mechanical with Impact | 85 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 85 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.0E+07 ohms·cm | ASTM D257 |
Surface Resistivity | 1.0E+05 ohms | ASTM D257 |
Static Decay(5000V to <50V) | < 0.01 Seconds | FTMS101B |
Shielding Effectivness @ 3Mm | 47 dB | SABIC Method |
Processing | Nominal Value |
Drying Temperature<Injection> | 85 - 90 °C |
Drying Time<Injection> | 3 - 4 hrs |
Maximum Moisture Content<Injection> | 0.04 % |
Melt Temperature<Injection> | 270 - 300 °C |
Nozzle Temperature<Injection> | 265 - 300 °C |
Front, Zone 3 Temperature<Injection> | 265 - 300 °C |
Middle, Zone 2 Temperature<Injection> | 260 - 300 °C |
Rear, Zone 1 Temperature<Injection> | 260 - 300 °C |
Mold Temperature<Injection> | 60 - 90 °C |
Back Pressure<Injection> | 4 MPa |
Screw Speed<Injection> | 30 - 100 rpm |